침지 산세 탱크의 산 농도가 표준을 초과하는지 여부를 결정하는 방법은 무엇입니까?

To determine whether the acid concentration of the immersion pickling tank exceeds the standard, a comprehensive analysis needs to be conducted in combination with the process standards, detection methods and actual reaction phenomena. The following are specific methods: 1. Concentration threshold based on process standards Each pickling process (such as steel rust removal, metal surface activation, etc.) has a clear acid concentration range, and the process documents or formula requirements need to be confirmed in advance. For example: Hydrochloric acid pickling: The commonly used concentration in the steel industry is 10%~20% (mass fraction). If the measured concentration is greater than 25% or less than 8%, it is considered to exceed the standard. Sulfuric acid pickling: The concentration is usually controlled at 15%~25%. Exceeding 30% may accelerate metal corrosion and produce a large amount of hydrogen. If it is less than 10%, the rust removal efficiency will be significantly reduced. Mixed acid (such as hydrochloric acid + hydrofluoric acid): It needs to be controlled according to a specific ratio (such as HCl:HNO₃=3:1). If the concentration of a single acid deviates from the formula by ±10%, it will be judged as abnormal. 2. Laboratory test method (precise quantification) The most reliable way to judge is to analyze the concentration of acid by sampling: Titration method (chemical analysis) Principle: Titrate the acid with a standard alkali solution (such as NaOH) and calculate the acid concentration by the amount of alkali consumed. Operation steps: Accurately draw 10mL of acid with a pipette, inject it into a conical flask, and add 2~3 drops of phenolphthalein indicator. Titrate with a known concentration of NaOH standard solution (such as 0.1mol/L) until the solution is slightly red and does not fade for 30 seconds, and record the consumed volume V (mL). Judgment standard: If the calculated result exceeds the process allowable range (such as ±5% fluctuation), it is considered that the concentration exceeds the standard. Density method (applicable to strong acid) Principle: The concentration of acid is linearly related to density (such as the higher the concentration of concentrated sulfuric acid, the greater the density), and the density is measured by looking up the table for comparison. Operation steps: Use a densitometer (or hydrometer) to directly immerse in the acid, read the scale value, and measure the temperature at the same time (need to be calibrated to the standard temperature of 20℃). Refer to the "Acid Concentration - Density Comparison Table" (e.g., hydrochloric acid at 20°C, 20% concentration corresponds to a density of about 1.09g/mL). If the measured value deviates from ±0.02g/mL, the concentration may be abnormal. pH detection method (applicable to dilute acid or mixed acid) principle: acid concentration is negatively correlated with pH value (the higher the concentration, the lower the pH), but it should be noted that strong acids (such as hydrochloric acid and sulfuric acid) have a dissociation degree close to 100% at high concentrations, and may not be sensitive to pH changes (e.g., 20% hydrochloric acid pH≈-0.3, 15% hydrochloric acid pH≈-0.1), and need to be used in combination with titration. The pH of weak acids (such as hydrofluoric acid) is nonlinearly related to concentration and needs to be converted through a standard curve. 3. On-site rapid detection method (convenient qualitative) is suitable for real-time monitoring or scenarios without laboratory conditions: pH test paper/test strips Use a glass rod to dip acid and drop it on the test paper, compare the pH value with the standard color card, and combine process experience to determine whether the concentration is abnormal (for example, in steel pickling, hydrochloric acid pH>1은 불충분 할 수 있습니다). 산 농도 시험지 (특수 시험지) 일부 제조업체는 특정 산 (예 : 염산 농도 시험지)에 대한 테스트 논문을 제공하며, 이는 산에 침지 된 후 색상을 발달시켜 농도 범위 (예 : 10%~ 15%, 15%~ 20%등)에 해당합니다. 전도도 방법 (휴대용 전도도 미터가 필요) 산 농도가 높을수록 이온 농도가 커지고 전도도가 높아집니다. "농도-컨덕션"곡선은 사전 보정되며 측정 된 값이 곡선에서 ± 10%씩 벗어나면 농도가 비정상임을 나타냅니다. 4. 산 농도가 비정상적 일 때 판단을 돕기위한 반응 현상을 관찰하고, 공작물과 산 사이의 반응은 심각한 예비 기반으로 사용될 수 있으며, 이는 판단의 예비 기반으로 사용될 수있다 : 불충분 한 농도 (낮은) 현상 : 공기의 표면에서 거품 생성 속도는 공기의 표면에 속도가 느려집니다. 녹 제거 또는 하강 시간이 크게 확장됩니다 (예 : 원래 30 분 안에 완료된 소아는 여전히 1 시간 이상 후에 표준을 충족하지 못합니다). 산 용액의 색 변화는 명백하지 않습니다 (예 : 강철의 산세에서 Fe²+ 농도는 느리게 증가하며 산 용액은 예상대로 밝은 녹색으로 변하지 않습니다). 과도한 농도의 현상 (표준 초과) : 반응은 폭력적이며, 많은 거품이 생성되고, 산 미스트가 휘발 당하면 (예를 들어, 염산 농도가 너무 높을 때, 탱크 위에 명백한 흰색 안개가 나타납니다). 공작물의 표면은 과도하게 부식되며, "검은 색"및 "구멍"또는 비정상적인 체중 감소가 나타납니다 (수소 손상의 위험 증가). 산 용액의 온도는 비정상적으로 상승합니다 (농축 황산을 희석 할 때 수술이 부적절한 경우 강한 열 방출로 인해 끓을 수 있습니다). V. 주파수 및 레코드 요구 사항 검사 빈도 : 정기적 인 생산에서 시프트 당 1 ~ 2 배 (8 시간). 공정 안정성이 열악하거나 연속적인 작동 인 경우 2 ~ 4 시간마다 한 번 검사해야합니다. 새로운 산 용액을 준비하거나, 산 용액을 첨가하거나, 공작물 재료를 교체 한 후에는 즉시 농도를 테스트해야합니다. 기록 및 추적 성 : 검출 시간, 농도 값, 테스터 및 표준을 초과하는지 여부를 기록하기 위해 "산 농도 검출 원장"을 설정합니다. 이상의 경우, 치료 조치 (예 : 산 첨가, 희석 또는 교체)를 표시해야합니다. 6. 예방 조치 안전 작동 : 산의 튀는 것을 피하기 위해 테스트 중에 산 방지 장갑과 고글을 착용하십시오. 산 샘플을 천천히 부어 튀는 것을 방지하십시오. 온도 영향 : 밀도 또는 전도도를 테스트 할 때 산 온도는 표준 온도 (예 : 20도)로 수정해야합니다. 그렇지 않으면 오류 (온도 증가 및 액체 밀도 감소)를 유발합니다. 복잡한 요인 : 산에 많은 양의 금속 이온 (Fe²+, Fe³+)이 포함 된 경우 밀도 또는 전도도에 영향을 줄 수 있으며 적정 방법을 결합하여 결과를 수정해야합니다. 상기 방법에 대한 포괄적 인 판단을 통해, 비정상적인 산 농도는 불충분 한 농도 또는 과도한 농도 (예 : 과도한 부식, 수소 폭발)로 인한 안전 사고로 인한 자격이없는 절인 효과를 피하기 위해 시간에 발견 될 수 있습니다.